【国外标准】 Standard Specification for Electric-Fusion-Welded Steel Pipe for Atmospheric and Lower Temperatures

This specification covers standard requirements for electric-fusion-welded steel pipe with filler metal added, for atmospheric and lower temperatures. The steel pipe shall be fabricated from a pressure vessel quality plate of several analysis and strength levels. Several grades and classes of pipe shall be provided. Grade shall designate the type of plate used while class shall designate the type of heat treatment performed during pipe manufacture. Class shall be designated as to whether the weld is radiographically examined, and as to whether the pipe is pressure tested. Steel samples shall undergo tension and transverse guided weld bend tests and conform to the specified mechanical requirements.1.1 This specification2 covers electric-fusion-welded steel pipe with filler metal added, fabricated from pressure vessel quality plate of several analyses and strength levels and suitable for high-pressure service at atmospheric and lower temperatures. Heat treatment may or may not be required to attain the desired properties or to comply with applicable code requirements. Supplementary requirements are provided for use when additional testing or examination is desired.1.2 The specification nominally covers pipe 16 in. [400 mm] in outside diameter or larger and of 1/4  in. [6 mm] wall thickness or greater. Pipe having other dimensions may be furnished provided it complies with all other requirements of this specification.1.3 Several grades and classes of pipe are provided.1.3.1 Grade designates the type of plate used as listed in 5.1.1.3.2 Class designates the type of heat treatment performed during manufacture of the pipe, whether the weld is radiographically examined, and whether the pipe has been pressure tested as listed in 1.3.3.1.3.3 Class designations are as follows (Note 1):Class Heat Treatment on Pipe Radiography, see Section Pressure Test, see: 10 none none none11 none 9 none12 none 9 8.313 none none 8.320 stress relieved, see 5.3.1 none none21 stress relieved, see 5.3.1 9 none22 stress relieved, see 5.3.1 9 8.323 stress relieved, see 5.3.1 none 8.330 normalized, see 5.3.2 none none31 normalized, see 5.3.2 9 none32 normalized, see 5.3.2 9 8.333 normalized, see 5.3.2 none 8.340 normalized and tempered, see 5.3.3 none none41 normalized and tempered, see 5.3.3 9 none42 normalized and tempered, see 5.3.3 9 8.343 normalized and tempered, see 5.3.3 none 8.350 quenched and tempered, see 5.3.4 none none51 quenched and tempered, see 5.3.4 9 none52 quenched and tempered, see 5.3.4 9 8.353 quenched and tempered, see 5.3.4 none 8.370 quenched and precipitation heat  treated none none71 quenched and precipitation heat  treated 9 none72 quenched and precipitation heat  treated 9 8.373 quenched and precipitation heat  treated none 8.3NOTE 1: Selection of materials should be made with attention to temperature of service. For such guidance, Specification A20/A20M may be consulted.1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. The inch-pound units shall apply unless the “M” designation of this specification is specified in the order.1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.